Component: Adding iron oxide red and zinc yellow pigment after
epoxy resin and seed fat alcoholized, adding dimethyl benzene and
butyl alcohol after rubbing with body pigment.
Application: Suitable to coating black metal, especially as primer
for surface of metal in costal areas and wet and torrid zone.
Properties: Hard film, good adhesion, increasing resistance to wet
pick and salt fog when used with etching primer.
Physical Parameter: Specific Gravity: 1.32kg/L
Color: Iron red
Theoretic Dosage: 0.16 kg/m2
Film Thickness: WFT: 100μ M DFT: 40μ M
Drying Time: 23± 2degrees, Dust-Free: ≤ 2 h, Non-dint Drying ≤ 18 h
Storage: 1 year
Flash Point: 30degrees
Application Parameter: Formula Ratio: One pot
Curing Time: Use directly after being opened
Pot Life: Infinite
Coating Method: High-pressure airless spray, hand brushing, roll
Diluent/ Dilution Ratio: Diluent for F102 epoxy coatings, Coating
Interval: 25degrees, Min. 24 h, Max. Infinite
Surface Treatment: Sand blasting must be made on surface of new
steel till qualified to SA2.5, If needing to protect steel
temporarily, appropriate shop primer should be used. Do clean the
wear shop primer and dirt before painting.
Recommended Layers: 2 layers of high-pressure airless spray, 80μ M
Post-Coat Accessory Coatings: Alkyd coatings and phenolic resin
Claim: The data in this Specification is derived from experiments
and practical applications, and can be regarded as a guide for
application. The title product is only for specialty application.
Otherwise we only guarantee the quality of the said coating itself
if it is used in other sectors undescribed herein or fresh sectors.