Component: Partial hydrolyzed alkyl silicon ester solution,
ultra-fine zinc powder, coloring pigment, additives and solvent,
etc. Two-component (A and B) package for this kind of primer.
Application: Maintenance primer for abrasive blasted steel,
warranty period: 9~12 months.
Properties: A kind of self-curing shop primer, excellent exterior
age resistance, good performances of cathodic protection,
resistance to rust, heat, cutting and welding. Suitable for using
with (in)organic coatings
Physical Parameter: Color: Gray
Specific Gravity: Approx. 1.67 kg/L
Theoretic Dosage: 0.1 kg/m2
Film Thickness: WFT: 60μ m DFT: 20μ m
Flash Point: 13degrees
Drying Time: 23± 2degrees, Dust-Free: ≤ 5 min, Hard Drying: ≤ 1 h,
Fully Curing: 3D
Storage: 1 year
Application Parameter: Formula Ratio: Component A (Paint Vehicle):
Component B (Curing Agent)= 3: 1
Curing Time: 25degrees, 0.5h
Pot Life: 25degrees, 8h
Coating Method: High-pressure airless spray, hand brushing, roll
Diluent/ Dilution Ratio: Diluent for F106 inorganic zinc coatings,
Surface Treatment: Sand blasting must be made on surface of steel
till qualified to SA 2.5 Standard of Sweden. Surface Asperity:
Post-Coat Accessory Coatings: Epoxy resin coatings, epoxy asphalt
coatings, chlorinated rubber coatings, acrylic resin coatings,
alkyd resin coatings, phenolic resin coatings, polyurethane
coatings and prechlorinated polythene coatings, etc.
Claim: The data in this Specification is derived from experiments
and practical applications, and can be regarded as a guide for
application. The title product is only for specialty application.
Otherwise we only guarantee the quality of the said coating itself
if it is used in other sectors undescribed herein or fresh sectors.
E06-28 Inorganic Zinc Silicate Primer Images